Magnesia carbon brick for converter

Is based on the use of different kiln parts and different conditions of use designed and manufactured using high-purity, high density, large crystal magnesia and high purity graphite as raw materials, high-pressure forming process of production. The product has high strength, good resistance to slag characteristics, widely used in lining, bag lining, especially for slag line, hot parts, out of brick and steel mouth seat the bottom of the seat cover and the ladle bricks. Can smelting conditions, ladle choose different brands in different parts of the MgO-C. Brand MgO CB.D(g/cm2)A.P()C.C.S(MPa)HMOR1400×30min(MPa)XL-MT18B72182.95±0.054358XL-MT16A74182.95±0.0534012XL-MT16B74162.95±0.0543510XL-MT14A76143.05±0.0544012XL-MT14B76143.00±0.0543510XL-MT12A78123.10±0.0554010XL-MT12B78123.05±0.055408XL-MT10 80103.05±0.055406